Study of Tensile Strength Test of Oxi-Asetyline Welding with the Addition of Borax to St 37 Steel
Studi Uji Kekuatan Tarik Hasil Las Oxi-Asetyline dengan Penambahan Boraks Pada Baja St 37
The use of welding in industry today is very broad, including shipping, machinery, construction and others. The aim of this research was to study the welding results of two types of metal with different melting points, namely low carbon steel ST37 with brass filler and borax added during the welding process using OAW (Oxygent Acetyline Welding) welding. The specimen size is 170 mm long, 50 mm wide and 8 mm thick. As for the test method with the addition of borax, then look at the results of the number of porosity, weld defects and differences in tensile strength in each specimen by conducting penetrant liquid testing and tensile testing with ASTM E-8 standards. The results of the penetrant liquid test showed that welding ST 37 steel using borax as an additional material produced welding with the smallest porosity and even no defects at all compared to specimens without using borax. The results of the tensile test show that the addition of borax has a tensile strength value of 2000 kgf / mm². This value is greater than without the addition of borax.
 Hardiansyah, T. 2018. Pengaruh Variasi Kuat Arus dan Wire Feed Rate Pada Baja Karbon Rendah Terhadap Kekuatan Tarik Hasil Pengelasan GMAW. Skripsi Tidak Diterbitkan. Malang: Fakultas Teknik Universitas Negeri Malang.A. Rezi and M. Allam, "Techniques in array processing by means of transformations, " in Control and Dynamic Systems, Vol. 69, Multidemsional Systems, C. T. Leondes, Ed. San Diego: Academic Press, 1995, pp. 133-180.
 Hartati, F, K. 2017. Analisis Boraks Secara Cepat, Mudah dan Murah pada Kerupuk. Surabaya: Universitas Dr. Soetomo H. Ayasso and A. Mohammad-Djafari, "Joint NDT Image Restoration and Segmentation Using Gauss–Markov–Potts Prior Models and Variational Bayesian Computation," IEEE Transactions on Image Processing, vol. 19, no. 9, pp. 2265-77, 2010. [Online]. Available: IEEE Xplore, http://www.ieee.org. [Accessed Sept. 10, 2010].
 Mukhadis, A. 2016. Metodologi Penelitian Kuantitatif: Bidang Pendidikan dan Contoh Aplikasinya. Malang: Aditya Media Publishing..
 Sugiyono. 2015. Metode Penelitian Kuantitatif, Kualitatif, dan R&D. Bandung: Alfabeta.
 J. R. Beveridge and E. M. Riseman, "How easy is matching 2D line models using local search?" IEEE Transactions on Pattern Analysis and Machine Intelligence, vol. 19, pp. 564-579, June 1997.
 E. H. Miller, "A note on reflector arrays," IEEE Transactions on Antennas and Propagation, to be published.
 ASTM International (E8–8M-09). 2010. Standart Test Methods for Tension Testing of Metalic Materials. United States of America
 Andinata, F., dkk. 2012. Pengaruh pH Larutan Elektrolit Terhadap Tebal Lapisan Elektroplating Nikel Pada Baja St 37. Surabaya: Universitas Negeri Surabaya
 Salahuddin Junus, Jurnal ROTOR, Volume 4 Nomor1, Januari 2011.
 Trinova Budi Santoso, Solichin, Prihanto Tri Hutomo, Pengaruh Kuat Arus Listrik. JURNAL TEKNIK MESIN, TAHUN 23, NO. 1, APRIL 2015