Analysis of Corrosion Breakdown Rate in Low Carbon Steel with Aluminum Coating
Analisa Laju Penembusan Korosi Pada Baja Karbon Rendah dengan Coating Aluminium
This study aims to analyze the corrosion penetration rate of low carbon steel with aluminium coating. The method used is the potentiodynamic method to determine the value of the corrosion rate. The corrosion medium used was HCl. The aluminium used is aluminium frame waste powder. The coating process is by dipping low carbon steel pipes into aluminium frame waste that had been liquefied in the Hot Dip Galvanizing (HDG) method of 700oC and immersion time of 45 seconds. The results of this study show that low carbon steel which has been coated with aluminum frame waste powder has a high corrosion rate which is proven to have a corrosion rate of 18,1808 mm/year. So that the corrosion rate is at an unacceptable level.
Natrium Klorida Menggunakan Inhibitor Ekstrak Daun Teh (Camelia Sinensis),” J. Fis. Unand, vol. 2, no. 3, pp. 204–211, 2013.
Pujiyantono, AN, “Karbon Rendah Dengan Seng Melalui Metode Hot Dip Galvanizing,” Universitas Negeri
M. Reigita and A. Setiawan, “Pengaruh Penambahan Serpihan Aluminium Sebagai Bahan Parsial Semen Terhadap Kuat Tekan dan Kuat Tarik Belah Beton,” Widyakala J., vol. 5, no. 1, p. 38, 2018, doi: 10.36262/widyakala.v5i1.100.
J., Trethewey, KR. 1991. Korosi. Jakarta: PT. Gramedia Pustaka Utama.
D. Ardhani, “Sintesis Inhibitor Korosi Dari Turunan Palm Kernel Oil Tersulfonasi Dan Uji Performanya Pada Baja,” Stud. Kim. Univ. Pertamina, 2020.
Ainu S. 2016, "Perilaku Korosi Baja AISI 1021 dan AISI 304 Dalam Berbagai Media Asam [Tugas Akhir]. Surabaya: Institut Teknologi Sepuluh November.